P355GH – P235GH Boiler Sheets? Differences?

p235gh quality

P355GH – P235GH Boiler Sheets? Differences?

P235GH and P355GH materials boiler sheets? also known as pressure? cap or pressure resistant? steels. Considering the general properties, it is seen that the weldability of both materials is good. side of that? they are resistant to high pressure and heat.

P235GH Quality Strength Values

P235GH quality material is in the group of unalloyed steel. Assist in the production of boilers in industrial areas. This material is used as a piece. In Turkey, only iron and steel factories in Ere? It is produced by. Erdemir 6335 is the quality code. Sellers also buy from here. ?the maximum carbon content in it? percent 0.16, manganese ratio? The phosphorus ratio is between 0.6 and 1.20. 0.025 and sulfur ratio? 0.015. Apart from this, it also contains elements such as nickel, molybdenum, copper, titanium. tensile strength? It is between 360 and 500 MPa. Can I resist bleeding? It is between 215 and 235 MPa and decreases as the thickness increases. It is a material suitable for cold forming.

P355GH Quality Strength Values

P355GH quality material pressurized. containers and hot liquid It is used in the production of carrying pipes. What is the carbon ratio in it? It is higher than P235. Creep resist?ml? and high groups steels? is between It is produced according to the EN 10028-2 standard. It contains elements such as 0.08-0.2 ratio of carbon, 0.4 ratio of silicon, 0.9-1.5 ratio of manganese and 0.3 ratio of carbon.

Yield and tensile strength? thick? as it changes. As the thickness increases, the yield strength? decreases. It is usually between 280 MPa and 355 MPa. Can I resist bleeding? It is one of the decisive mechanical properties for the materials to be used in production. The high yield strength of the load-bearing materials required. However, it is undesirable for the materials to be formed to have high yield values. Can I resist bleeding? dividing the tensile strength of the material figure alma kabiliyetini belirleyen de?er bulunur. P355 kalite malzemenin çekme dayan?m? ise 470 MPa ile 650 MPa aras?nda de?i?ir. Yüzde uzama miktar? ise %20?dir.

P235GH and P355GH Is? hold on

While the P235 material can withstand temperatures of 150-200 degrees P355 material to temperatures of 400 degrees It remains intact even when exited. Because of this feature? It is used in the production of materials that will be exposed to high temperatures such as boilers and pipes. P235, on the other hand, is not the main material but an auxiliary material during boiler production. used as.

 